Economical silicon-on-silicon hybrid wafer assembly

ABSTRACT

An economical hybrid wafer utilizing a lower-quality, lower cost transfer substrate to support a higher-quality thin film. A high-quality thin film ( 2101 ) is separated from a donor wafer ( 2100 ) and bonded to a transfer, or target, substrate ( 46 ). The donor wafer is preferably single-crystal silicon optimized for device fabrication, while the transfer substrate provides mechanical support. The thin film is not grown on the transfer substrate, and thus defects in the transfer substrate are not grown into the thin film. A low-temperature bonding process can provide an abrupt junction between the target wafer and the thin film.

CROSS REFERENCE TO RELATED APPLICATIONS

This application claims the benefit of U.S. Application Ser. No. 60/046,276, filed May, 12, 1997, the disclosure of which is incorporated by reference.

This application claims priority from the provisional patent application entitled A CONTROLLED CLEAVAGE PROCESS AND RESULTING DEVICE, filed May 12, 1997 and assigned Application Ser. No. 60/046,276, the disclosure of which, is hereby incorporated in its entirety for all purposes. This application is being filed on the same date as related Application No. Ser. No. 09/026,117 entitled “AN ECONOMICAL SILICON-ON-SILICON HYBRID WAFER BONDING PROCESS USING A THIN FILM”.

BACKGROUND OF THE INVENTION

The present invention relates to the manufacture of substrates. More particularly, the invention provides a technique for manufacturing a silicon-on-silicon substrate assembly. The assembly consists of two substrates that are bonded together for use in the fabrication of a hybrid substrate for semiconductor integrated circuits, for example. However, it will be recognized that the invention has a wider range of applicability. For example, it can also be applied to other substrates for multi-layered integrated circuit devices, three-dimensional packaging of integrated semiconductor devices, microelectromechanical systems (“MEMS”), sensors, actuators, solar cells, biological and biomedical devices, and the like.

Wafers for electronic device fabrication are often cut from an ingot, or boule, of material with an abrasive saw. The wafer often serves as both a mechanical support and semiconductor material to form electronic devices in or on. One of the most common examples of this is cutting silicon wafers from a silicon ingot. The wafers are typically polished to a very fine surface finish after “lapping” the wafer to remove the mechanical damage left by the abrasive saw, and after “backlapping” the other side of the wafer to remove saw damage and to produce a wafer of the desired thickness, or to intentionally introduce strain in the wafer that improves the “gettering” of impurities. Gettering typically involves providing a trapping site for certain mobile impurity species that can degrade the performance of the devices in the integrated circuit. The impurities diffuse, or migrate, to the gettering sites, where they are trapped, thus lowering their concentration in the area of the devices.

In some processes, devices are fabricated directly in or on the silicon wafer. In other processes, a layer of semiconductor material is grown, for example by epitaxy, on the wafer. An epitaxial layer may provide lower impurity concentrations, or be of a different semiconductor type than the wafer. The devices are formed in what is known as the “active” layer, which is typically only a few microns thick.

Unfortunately, epitaxial layers have some associated problems that can affect wafer yield and device performance. Epitaxial layers that are grown on a substrate typically adopt the crystalline structure of the substrate. In most cases, the substrate is a single crystal of a particular orientation. However, the most favored crystallographic orientation for growing an epitaxial layer may not be the most favored crystallographic orientation for forming semiconductor devices. Additionally, surface defects or contamination on the surface of the substrate can lead to “pipes”, “spikes”, and other types of defects in the epitaxial layer. Often, a single defect will ruin a particular circuit, or cell, on a substrate. As the size of the cells get bigger and more complex, the chance that any particular cell will fail because of a defect in the epitaxy layer increases. The size of the cells generally increase, given a particular processing technology, as the device count increases, which usually indicates an increase in circuit complexity and functionality.

Another problem associated with epixatial layer configurations is the diffusion of doping species from the substrate to the epitaxial layer, or vice versa, and the autodoping of the epitaxial layer by doping species released by the substrate into the epitaxial growth environment. Unlike the mobile impurities that are trapped at gettering sites, doping species are typically introduced into the silicon crystal for a desired purpose. For example, the silicon substrate may have a high concentration of n-type impurities to reduce series resistance through the substrate, while the epitaxial layer has a low concentration of n-type impurities to allow efficient devices to be fabricated in the epitaxial layer. Alternatively, the substrate may be n-type impurities and the epitaxial layer may be p-type. In many applications it is desirable to have an abrupt junction between the epitaxial layer and the substrate; however, diffusion of the doping species across the interface degrades this abrupt junction.

Silicon epitaxy layers can be grown from a variety of sources, each with its own advantages and disadvantages. For example, silicon tetrachloride is typically used for growing epitaxial layers greater than 3 microns thick, but requires temperatures up to 1250° C., which results in significant autodoping and outdiffusion. Silane can be used to grow epitaxial layers around 1000° C., but it typically is used to grow only very thin layers, as it tends to pyrolyze and coat the chamber walls, requiring frequent cleaning. The rate of growth with silane is also much lower than with other sources, thus making it difficult to grow layers of epitaxial silicon more than about 1 micron thick.

The size of silicon wafers also continues to increase. Many state-of-the-art semiconductor devices are fabricated on 8-inch silicon wafers. Twelve-inch wafers are available, and the semiconductor fabrication industry is moving toward using wafers of this size, but, as with most changes in technology, the industry must solve some problems first. One of the problems is that growing a high-quality epitaxial layer on large wafers is very difficult. Some conventional processes do not have a sufficient yield of good wafers through the epitaxial growth process to make using a 12-inch wafer economically attractive, and even 8-inch wafer processes suffers from yield loss. These processes also generate a number of “scrap” wafers. The cost of a 12-inch substrate can be quite high, making yield loss and scrap generation very costly.

From the above, it is seen that a technique for providing an improved wafer that is cost effective is desirable.

SUMMARY OF THE INVENTION

According to the present invention, a technique for applying a thin film of material to a target wafer is provided. This technique separates thin films of material from a high-quality donor substrate by implanting particles, such as hydrogen ions, into the donor substrate, and then separating a thin film of the high-quality material above the layer of implanted particles. The thin film can be bonded to a lower-quality target wafer that provides mechanical support to form an economical hybrid substrate.

In a specific embodiment, the present invention provides a process for forming a film of material from a high-quality donor substrate using a controlled cleaving process. That process includes a step of introducing energetic particles (e.g., charged or neutral molecules, atoms, or electrons having sufficient kinetic energy) through a surface of a donor substrate to a selected depth underneath the surface, where the particles are at a relatively high concentration to define a thickness of donor substrate material (e.g., thin film of detachable material) above the selected depth.

The surface of the donor wafer is then attached to a target wafer using, a low-temperature bonding process to form an intermediate substrate assembly. The target wafer can be a single crystal, polycrystalline, or amorphous silicon substrate. Energy is applied to a selected region of the donor substrate material to initiate a controlled cleaving action in the donor substrate, whereupon the cleaving action is made using a propagating cleave front(s) to free the donor material, which adheres to the target wafer, from a remaining portion of the donor substrate. The thin film is then permanently bonded to the target wafer, typically with a high-temperature annealing process to form a hybrid silicon wafer suitable for integrated circuit fabrication, among other uses. The lower-cost, lower-quality target wafer portion of the hybrid silicon wafer provides the mechanical support for the hybrid wafer, while the thin film portion of the hybrid wafer provides a high-quality material for the formation of electronic devices.

In another embodiment, a layer of microbubbles is formed at a selected depth in a donor substrate, which is then bonded to a target wafer. The substrate is globally heated and pressure in the bubbles eventually shatters the substrate material generally in the plane of the microbubbles, separating a thin film of silicon from the substrate.

The present invention achieves these benefits and others in the context of known process technology. However, a further understanding of the nature and advantages of the present invention may be realized by reference to the latter portions of the specification and attached drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

FIGS. 1-3 are simplified diagrams illustrating a controlled cleaving technique according to an embodiment of the present invention;

FIGS. 4-6 are simplified diagrams illustrating a blister-separation technique according to another embodiment of the present invention;

FIGS. 7-10 are simplified diagrams illustrating a method of forming a silicon-on-insulator substrate according to the present invention;

FIG. 11 is a simplified representation of doping concentration versus depth from a wafer surface for representative epitaxial and thin film bonded substrates;

FIG. 12 is a simplified diagram of a wafer polishing process;

FIGS. 13 is a simplified cross section of a hybrid wafer with an adhesion layer; and

FIG. 14 is a simplified cross section of a hybrid wafer with a barrier layer and a gettering layer.

DESCRIPTION OF SPECIFIC EMBODIMENTS

The present invention provides a technique for removing a high-quality thin film of material from one substrate and bonding it to a second substrate of lesser quality, thus using the high-quality material where it contributes to the value of the wafer, and lower cost material as the mechanical support. The high-quality material generally has specifications making it suitable for the fabrication of integrated circuit devices. The lesser-quality substrate is generally not suitable for direct use in the fabrication of integrated circuit devices. The thin film of material forms a hybrid substrate with the second substrate and can substitute for a wafer with an epitaxial layer, or a conventional homogeneous wafer. The invention will be better understood by reference to the Figs. and the descriptions below. The description begins with explanations of thin film removal processes before discussing the wafer bonding processes and resultant structures.

1. Controlled Cleaving Techniques

In a controlled cleaving process, a cleave is initiated by subjecting the material with sufficient energy to fracture the material in one region, causing a cleave front, without uncontrolled shattering or cracking. The cleave front formation energy (E_(c)) must often be made lower than the bulk material fracture energy (E_(mat)) at each region to avoid shattering or cracking the material. The directional energy impulse vector in diamond cutting or the scribe line in glass cutting are, for example, the means in which the cleave energy is reduced to allow the controlled creation and propagation of a cleave front. The cleave front is in itself a higher stress region and once created, its propagation requires a lower energy to further cleave the material from this initial region of fracture. The energy required to propagate the cleave front is called the cleave front propagation energy (E_(p)). The relationship can be expressed as:

E _(c) =E _(p)[cleave front stress energy]

A controlled cleaving process is realized by reducing F_(p) along a favored direction(s) above all others and limiting the available energy to be below the E_(p) of other undesired directions. In any cleave process, a better cleave surface finish occurs when the cleave process occurs through only one expanding cleave front, although multiple cleave fronts do work.

This technique uses a relatively low temperature, typically less than about 400° C. for silicon, during the controlled cleaving process of the thin film to reduce temperature excursions of the separated film, donor substrate, or multi-material films according to other embodiments. This lower temperature approach allows for more material and process latitude such as, for example, cleaving and bonding of materials having substantially different thermal expansion coefficients. The energy or stress in the substrate is limited to a value below a cleave initiation energy, which generally removes a possibility of creating random cleave initiation sites or fronts. This reduces cleave damage (e.g., pits, crystalline defects, breakage, cracks, steps, voids, excessive roughness) often caused in pre-existing techniques. Moreover, a controlled-cleavage method reduces damage caused by higher than necessary stress or pressure effects and nucleation sites caused by the energetic particles as compared to other techniques.

FIG. 1 is a simplified cross-sectional view diagram of a substrate 10 according to the present invention. As merely an example, substrate 10 is a high-quality single-crystal silicon wafer which includes a material region 12 to be removed, which is a thin relatively uniform film derived from the substrate material. A high-quality wafer has a desired doping concentration, typically expressed as resistivity, a uniform doping concentration, typically expressed as resistivity gradient, low impurity concentration, typically expressed as minority carrier lifetime, and low dislocation density. The silicon wafer 10 includes a top surface 14, a bottom surface 16, and a thickness 18. Substrate 10 also has a first side (side 1) and a second side (side 2) (which are also referenced below in the Figs.). Material region 12 also includes a thickness 20, within the thickness 18 of the silicon wafer.

Hydrogen ions are implanted 22 through the top surface 14 of the silicon wafer to a selected depth 24, which defines the thickness 20 of the material region 12, termed the thin film of material. The ions can be implanted by a variety of techniques, including beam line ion implantation, plasma immersion ion implantation (“PIII”), or ion shower. Beam line ion implantation can be performed with equipment manufactured from companies such as Applied Materials, Eaton Corporation, Varian, and others. Examples of plasma immersion implantation techniques are described in “Recent Applications of Plasma Immersion Ion Implantation,” Paul K. Chu, Chung Chan, and Nathan W. Cheung, SEMICONDUCTOR INTERNATIONAL, pp. 165-172, June 1996, and “Plasma Immersion Ion Implantation—A Fledgling Technique for Semiconductor Processing,” MATERIALS SCIENCE AND ENGINEERING REPORTS: A REVIEW JOURNAL, pp. 207-280, P. K. Chu, S. Qin, C. Chan, N. W. Cheung, and L. A. Larson, Volume R17, Nos. 6-7, (Nov. 30, 1996), which are both hereby incorporated by reference for all purposes.

Hydrogen ions are desirable because they easily travel through the substrate material to the selected depth without substantially damaging the material region that the particles traverse through. The particles can also be derived from compounds such as gases, e.g., hydrogen gas, water vapor, methane, and hydrogen compounds, and other light atomic mass particles. Alternatively, other ions or combinations of ions may be used, depending on the material of the donor substrate, the thickness of the film to be removed, and the acceptable level of damage remaining; in the thin film after processing.

Implantation dose ranges from about 10¹⁵ to about 10¹⁸ atoms/cm², and preferably the dose is greater than about 10¹⁶ atoms/cm². Implantation energy ranges from about 1 KeV to about 1 MeV , and is generally about 50 KeV. Implantation temperature ranges from about −200 to about 600° C., and is preferably less than about 400° C. to maintain the implanted stress and to reduce the escape of the implanted particles (e.g. via diffusion). The hydrogen ions can be selectively introduced into the silicon wafer to the selected depth at an accuracy of about ±0.03 to ±0.05 microns.

Effectively, the implanted particles add stress or reduce fracture energy along a plane parallel to the top surface of the substrate at the selected depth. The energies depend, in part, upon the implantation species and conditions. These particles reduce a fracture energy level of the substrate at the selected depth. This allows for a controlled cleave along the implanted plane at the selected depth.

FIG. 2 is a simplified energy diagram 200 along a cross-section of the implanted substrate 10 according to the present invention. The diagram is merely an illustration and should not limit the scope of the claims herein. The simplified diagram includes a vertical axis 201 that represents an energy level (E) (or additional energy) to cause a cleave in the substrate. A horizontal axis 203 represents a depth or distance from the bottom of the wafer to the top of the wafer. After implanting particles into the wafer, the substrate has an average cleave energy represented as E 205, which is the amount of energy needed to cleave the wafer along various cross-sectional regions along the wafer depth. The cleave energy (F_(c)) is equal to the bulk material fracture energy (E_(mat)) in non-implanted regions. At the selected depth 20, energy (E_(cz)) 207 is lower since the implanted particles essentially break or weaken bonds in the crystalline structure (or increase stress caused by a presence of particles also contributing to lower energy (ED_(cz)) 207 of the substrate) to lower the amount of energy needed to cleave the substrate at the selected depth. This takes advantage of the lower energy (i.e. increased stress) at the selected depth to cleave the thin film in a controlled manner.

FIG. 3 is a simplified cross-sectional view of an implanted substrate 10 using selective positioning of cleave energy according to the present invention. This diagram is merely an illustration, and should not limit the scope of the claims herein. The implanted wafer undergoes a step of selective energy placement or positioning or targeting which provides a controlled cleaving action of the material region 12 at the selected depth. In this instance, the impulse is localized heating provided by a laser, although other heat sources, such as a heat lamp, or cold sources can be utilized. In another embodiment, a mechanical impulse is provided by twisting the target substrate with respect to the donor substrate, which generates maximum stress at the perimeter of the assembly, and minimum stress at the center. Of course, the type of source used depends upon the application.

Before locally heating the assembly, the stress in the implanted region was increased toward the energy level necessary to initiate the cleaving action without initiating the cleaving action. The global energy state of the substrate was raised by heating one side of the substrate to an intermediate temperature of about 350° C. with a heat lamp, or the substrate can be cooled, or differentially heated or cooled, that is a thermal gradient may be established across the assembly.

The removed material region provides a thin film of silicon material for processing. The silicon material possesses limited surface roughness and desired planarity characteristics for use in a silicon-on-silicon substrate. In certain embodiments, the surface roughness of the detached film has features that are less than about 40 nm root-mean-squared (“RMS”). Accordingly, the present invention provides thin silicon films which can be smoother and more uniform than other techniques.

2. A Blister-Separation Technique

FIGS. 4-6 are simplified cross sections of a thin film of material being separated from a wafer according to a blister-separation method, such as a process known as “Smart Cut.” An example of an implantation blister-separation method is described in U.S. Pat. No. 5,374,564, entitled Process For The Production Of Thin Semiconductor Material Films, by Michel Bruel, issued Dec. 20, 1994.

FIG. 4 shows a monocrystalline donor wafer 40 with a blister layer 41. The blister layer was formed by implanting gas-forming ions, such as hydrogen ions, into the donor wafer, which is oriented such that a crystalline plane, or cleavage plane, is approximately parallel to the blister layer. For example, a dose of about 10¹⁶ cm² hydrogen ions implanted into a {100} silicon wafer at 150 KeV formed a blister layer approximately 1.2 μm below the top surface 42 of the donor wafer 40. It is believed that the implanted hydrogen ions capture electrons to form hydrogen atoms, which in turn form diatomic hydrogen gas. The hydrogen gas starts to form, a layer of microbubbles in the blister layer, which is parallel to a cleaving plane of the donor wafer. When the wafer is heated, gas pressure builds within the blister layer, and a thin layer 45 of the donor wafer will split off along the cleavage plane.

While other gas-forming ion sources may be used, such as helium, neon, krypton, and xenon sources, hydrogen is advantageous. The braking process of hydrogen ions in silicon is an electronic, rather than nuclear, phenomena. This allows for a relatively high dosage to be implanted with relatively little damage to the silicon lattice, as compared to implanting similar doses of heavier ions. The electronic braking also provides a smaller range of distribution of implanted ions than would typically be obtained when implanting a heavier ion. This makes it possible to obtain suitable blister formation at a moderate implanted dose, and to separate a flyer of silicon with a relatively smooth surface.

The thickness of the thin layer may be determined by appropriately choosing the implant energy. The expected thickness in {100} silicon has been calculated using the public-domain “TRIM” modeling software developed by J. Zeigler, as shown in Table 1.

TABLE 1 ENERGY (KeV) 10 50 100 150 200 500 1000 Film Thickness (μm) 0.14 0.5 0.88 1.27 1.72 5.59 15.67

FIG. 5 shows a target wafer 46 bonded to the donor wafer 40. The target wafer provides support to the thin film 45 of silicon that will be blistered off of the donor wafer. The target wafer is a silicon wafer. The donor wafer may be beta bonded to the target wafer by a variety of methods, as described above. As above, it is desirable that the beta bonding method used not induce separation of the thin film unless that separation is intended. After beta bonding, heat treating the wafer assembly causes pressure to build up in the hydrogen gas bubbles that have formed in the donor substrate, to separate the top layer of silicon (about 1-15 microns thick) from the donor wafer. The beta-bonding, heat treating, and annealing can be performed in a continuous thermal process, if desired.

FIG. 6 shows the thin film 45 of silicon attached to the target wafer 46 after separating the thin film from the donor wafer.

3. Silicon-On-Silicon Process

A process for fabricating a silicon-on-silicon substrate according to the present invention may be briefly outlined as follows:

(1) Provide a donor silicon wafer with a highly polished surface;

(2) Introduce particles into the silicon wafer through the highly polished surface to a selected depth to define a thickness of silicon film;

(3) Provide a target substrate material with a highly polished surface;

(4) Prepare the surface of the donor wafer and/or the surface of the target wafer for beta bonding the donor wafer to the target wafer (optional);

(5) Beta bond the donor silicon wafer to the target substrate material by joining the two highly polished surfaces;

(6) Separate a thin film of material from the donor substrate, the thin film of material adhering to the target substrate;

(7) Anneal the hybrid substrate of the thin film and the target substrate to complete bonding of the two layers together;

(8) Polish a surface of the thickness of silicon film (optional).

This sequence of steps is merely an example and should not limit the scope of the claims defined herein. Further details with regard to the above sequence of steps are described in below in references to the Figs.

FIGS. 7-10 are simplified cross-sectional view diagrams of substrates undergoing a fabrication process for a silicon-on-silicon wafer according to the present invention. The process begins by providing a high-quality semiconductor substrate similar to the silicon wafer 2100, as shown by FIG. 7. For example, the substrate should have a dislocation density less than 1/cm² and have electron and hole mobilities similar to those of device-grade epitaxial silicon layers. Other types of donor material, including lower-quality material, may be appropriate for other applications. The donor substrate includes a material region 2101 to be removed, which is a thin, relatively uniform film derived from the substrate material. The silicon wafer includes a top surface 2103, a bottom surface 2105, and a thickness 2107. Material region also includes a thickness (Z₀) within the thickness 2107 of the silicon wafer above a layer 2111 of hydrogen ions or microbubbles, depending on the process used.

Hydrogen ions 2109 are implanted through the polished top surface of the silicon wafer to a selected depth, which defines the thickness of the material region, termed the thin film of material. As shown, the hydrogen ions (or microbubbles, depending on the process) have a desired concentration 2111 at the selected depth (Z₀). A variety of techniques can be used to implant the ions into the silicon wafer. These techniques include ion implantation using, for example, beam line ion implantation equipment manufactured from companies such as Applied Materials, Eaton Corporation, Varian, and others. Alternatively, implantation occurs using a plasma immersion ion implantation (“PIII”) technique or an ion shower technique. Of course, techniques used depend upon the application.

The process uses a step of preparing the implanted donor silicon wafer to bond to a workpiece, or target, silicon wafer, as illustrated in FIG. 8. The target silicon wafer does not require the same characteristics and specifications as the donor wafer because the target primarily provides mechanical support to the thin film that has excellent electrical and device fabrication properties. Thus, the target wafer can be of lesser quality, and therefore less expensive, than the donor wafer. In some embodiments, the target wafer could be a wafer that was rejected for conventional device fabrication processes, or grown by a different process. For example, the target wafer could be grown by a continuous-liquid-feed Czochralski method, while the donor wafer is high-purity material grown by a float zone method. Alternatively, the target wafer could be a polysilicon wafer, as might be cut from a polysilicon feed rod, while the donor wafer is high-quality single crystal.

The silicon wafers are first “beta bonded” using a low temperature thermal step. Beta bonding is a relatively weak bonding process that joins the donor substrate to the target substrate. It is believed that beta bonding arises from electrostatic, or van der Waals, forces. Beta bonding produces a joint between the donor substrate and the target substrate for the target substrate to act as a mechanical support for the thin film when it is subsequently separated from the donor wafer. Beta bonding is generally not robust enough to join the thin film to the target wafer during subsequent wafer processing, such as lapping, polishing, or dicing operations, but is sufficient to hold the thin film to the target wafer until the assembly can be annealed and securely bonded.

Prior to beta bonding, the surfaces of the wafers are stripped of native or residual oxide and thoroughly cleaned, such as with an RCA-I and RCA-II cleaning sequence. An example of a solution used to clean the wafer is a mixture of H₂O₂—H₂SO₄. A dryer dries the wafer surfaces to remove any residual liquids or particles from the wafer surfaces. In an alternative process, the clean silicon surfaces of the wafers are dipped in hydrofluoric acid, allowing the surfaces to become hydrophillic, and thus attractive to each other.

The cleaned and/or activated surfaces are then pressed together under moderate pressure. Using a low temperature beta bonding process (e.g. less than about 400° C.) generally ensures that the implanted particles do not initiate a fracture, or not diffuse or outgas. In one aspect, the low temperature bonding process occurs by a self-bonding process.

Alternatively, a self-bonding process occurs by activating one or both of the wafer surfaces to be bonded by plasma cleaning. In particular, plasma cleaning activates the wafer surface using a plasma derived from gases such as argon, ammonia, neon, water vapor, and oxygen. It is believed that the plasma cleaning step activates the surface of the wafer by creating dangling silicon bonds. The activated target wafer surface 2203 is placed against a face of the donor wafer surface 2103, which will create a layer-to-layer interface. The wafers are in a sandwiched structure having exposed wafer faces, and the target wafer still has a desired concentration of particles 2111 intact. A selected amount of pressure is placed on each exposed face of the wafers to self-bond one wafer to the other.

After beta bonding the wafers into a substrate assembly 2300, as shown in FIG. 9, the target wafer 46 and the donor wafer 2100 are joined at a layer-to-layer interface 2305. The particles or microbubbles still form a separation region 2111 in the donor wafer. After beta bonding, the substrate assembly 2300 is processed to separate the thin film 2101 from the donor wafer 2100.

FIG. 10 shows a final bonding, or annealing, step occurs between the target wafer and thin film of material to form a hybrid wafer 2410. These embodiments often require high temperatures (e.g., above 700° C.). The final bonding step creates a strong bond between the thin film and the target substrate. It is believed that covalent bonds form between the two layers of silicon when the assembly is subjected to a sufficiently high temperature for a sufficient period of time, for example at 1,000° C. for approximately 1 hour. Lower temperatures generally require longer periods of time for the same degree of bonding to take place. During the annealing process, a thin film of thermal oxide 2406 may grow on the thin film 2101. The final bonding process can provide an ohmic connection between the thin film and the target wafer, as well as a robust mechanical bond that can withstand subsequent wafer processing.

The degree of annealing and time-temperature product used to obtain the desired result can be chosen according to the necessary bond strength and requirements of the thin film layer. For example, a lower temperature, longer anneal may limit outdiffusion from the target wafer into the thin film compared to a higher temperature, shorter anneal. This enables the formation of an abrupt-junction hybrid silicon wafer in which the bonding process does not significantly alter the doping gradient at the layer-to-layer interface. Furthermore, because the thin film is beta bonded to the target wafer and overlaying the target wafer, and the thin film is not grown, as is an epitaxial layer, no autodoping occurs as in epitaxial growth.

FIG. 11 is a simplified representation of a dopant concentration versus distance from the surface of a wafer for an epitaxial layer grown over a heavily doped substrate 110 and the expected dopant concentration for a bonded hybrid wafer 112 having a thin film the same thickness as the epitaxial layer, and the same intentional doping level 114. The epitaxial layer shows a gas-phase autodoping tail 116 and more pronounced solid-state outdiffusion 118 than the lesser outdiffusion 120 occurring in the hybrid wafer due to the bonding process. The autodoping tail is not indicated for the bonded hybrid wafer as the thin film is not grown in a gaseous environment, as is the epitaxial layer. Thus the bonded hybrid wafer produces an abrupt junction between the thin film and the target substrate that is not obtained with conventional epitaxial processes. For example, the transition width between the heavily doped substrate (e.g. 10²⁰/cm³ concentration) to the lightly doped surface layer (e.g. 10¹⁵/cm³ concentration) should be less than about 1 micron, or less than about 0.7 microns, or less than about 0.5 microns.

Alternatively, the two silicon surfaces can be bonded by applying voltage between the two layers to establish a current flow through the hybrid wafer. The electric current heats the wafers to induce a bonding between the wafers. This technique limits the amount of crystal defects introduced into the silicon wafers during the bonding process, since substantially no mechanical force is needed to initiate the bonding action between the wafers. Damage may also be limited because the localized heating at the layer-layer interface is greater, due to increased series, resistance in this region, than in the bulk of either the target substrate or the thin film.

After bonding the wafers, silicon-on-silicon has a target substrate with an overlying film of silicon material, as also illustrated in FIG. 10. The detached surface of the film of silicon material 2404 is often rough and may need finishing for some applications. Finishing occurs using a combination of grinding and/or polishing techniques. In some embodiments, such as when the thin film has been separated using a blister-separation method, the detached surface may undergo a step of grinding, or lapping, before the polishing step.

If the thin film was separated using a controlled cleavage process, the relative smooth and fracture-free surface allows chemical mechanical polishing or planarization (“CMP”) techniques without a prior lapping step, as illustrated by FIG. 12. In CMP, a slurry mixture is applied directly to a polishing surface 2501 which is attached to a rotating platen 2503. This slurry mixture can be transferred to the polishing surface by way of an orifice, which is coupled to a slurry source. The slurry is often a solution containing a mild abrasive and an oxidizer, e.g., H₂O₂, KIO₃, or ferric nitrate. The abrasive is often very fine borosilicate glass, titanium dioxide, titanium nitride, aluminum oxide, aluminum trioxide, iron nitrate, cerium oxide, silicon dioxide (colloidal silica), silicon nitride, silicon carbide, graphite, diamond, and any mixtures thereof. This abrasive is mixed in a solution of deionized water and oxidizer or the like.

FIG. 13 is a simplified cross section of an economical hybrid wafer according to another embodiment of the invention utilizing an adhesion layer 130 between the thin film 2101 and the target wafer 46. The adhesion layer can be a very thin layer of titanium, tungsten, or titanium-tungsten, for example, applied to either the target wafer or to the donor wafer, preferably by a low-temperature process after implantation. In some embodiments, the adhesion layer is very thin, only a few atomic layers thick, that alloys with the silicon during the bonding process to form a very thin region of silicon alloy. The adhesion layer improves boding between the thin film and the target wafer, and allows more through bonding at lower temperatures.

FIG. 14 shows a simplified cross section of a hybrid wafer in which a low-quality, low-purity target wafer 141 is bonded to a high-quality thin film layer 143 with a barrier layer 145. In this embodiment, the layer is thick enough so that not all of the layer alloys with the silicon, and a barrier layer 145 remains after bonding. The barrier layer can prevent impurities from the target wafer from diffusing into the thin film during wafer processing The barrier layer 145 has adhesion regions 147, 149 with both the thin film 143 and the target wafer 141. Another advantage of the barrier layer is that it can also planarize the surface of the wafer to which is applied, thus reducing the need to highly polish the wafer. In this embodiment, an optional gettering layer 151, of polysilicon or Si-Ge, for example, was formed on the donor wafer prior to cleaving. The polysilicon layer acts as a gettering layer to remove mobile impurity species from the active regions in the thin film, while the barrier layer prevents additional impurities from entering the thin film. A layer of silicon-germanium could be used as a gettering layer instead of a layer of polysilicon, as could other layers.

While the above is a full description of the specific embodiments, various modifications, alternative constructions and equivalents may be used. Although the above has been described in terms of silicon-on-silicon, the present invention can be used with a variety of other multi-layered substrates. For example, the invention can be applied to silicon-on-insulator or other multi-layered substrates. Therefore, the above description and illustrations should not be taken as limiting the scope of the present invention which is defined by the appended claims. 

What is claimed is:
 1. A hybrid silicon wafer assembly, said assembly comprising: a high-quality single-crystal silicon thin film coupled to a lower-quality silicon transfer substrate.
 2. The assembly of claim 1 wherein the high-quality single-crystal silicon thin film is bonded to the lower-quality silicon transfer substrate.
 3. The assembly of claim 1 wherein the lower-quality silicon transfer substrate comprises polysilicon.
 4. The assembly of claim 1 wherein the lower-quality transfer substrate comprises single-crystal silicon, the high-quality single crystal silicon thin film having a first defect density at least ten times less than a second defect density of the lower-quality substrate.
 5. The assembly of claim 4 wherein the first defect density and the second defect densities include dislocation densities.
 6. The assembly of claim 1 wherein the lower-quality transfer substrate has a first minority carrier lifetime at least ten times less than a second minority carrier lifetime in the high-quality single-crystal thin film.
 7. The assembly of claim 1 wherein the lower-quality transfer substrate has a first carrier mobility at least ten times less than a second carrier mobility in the high-quality single-crystal thin film.
 8. The assembly of claim 1 further comprising an adhesion layer disposed between the high-quality single-crystal silicon thin film and the lower-quality silicon transfer substrate.
 9. The assembly of claim 8 wherein the adhesion layer comprises a silicide-forming metal.
 10. The assembly of claim 9 wherein the silicide-forming metal includes titanium.
 11. The assembly of claim 9 wherein the adhesion layer comprises tungsten.
 12. The assembly of claim 8 wherein the adhesion layer comprises an oxide.
 13. The assembly of claim 1 further comprising a barrier layer disposed between the high-quality single-crystal silicon thin film and the lower-quality silicon transfer substrate.
 14. The assembly of claim 13 wherein the barrier layer comprises a silicide-forming metal.
 15. The assembly of claim 14 wherein the barrier layer comprises titanium.
 16. The assembly of claim 14 wherein the barrier layer comprises tungsten.
 17. The assembly of claim 13 wherein the barrier layer comprises an oxide.
 18. The assembly of claim 13 further comprising a gettering layer disposed between the barrier layer and the high-quality single-crystal silicon thin film.
 19. The assembly of claim 18 wherein the gettering layer comprises polysilicon.
 20. The assembly of claim 18 wherein the gettering layer comprises silicon-germanium. 